Megalon® 235ML
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Mega Polymers |
| Trademark: | Megalon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xh24u5_Megalon-235ML.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon Type-6, with 35% mineral reinforcement for injection molding applications. Megalon® mineral reinforced nylons offer a good balance of strength, rigidity, and significant improvement in thermal and creep resistance Vs. un-filled Type-6 nylon. The mineral additive also reduces warp and maintains uniform dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.80 to 1.1 | % | |
| Water Absorption | ASTM D570 | ||
| 24 hr | 1.1 | % | |
| Saturation | 5.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 89.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 10 | % | ASTM D638 |
| Flexural Modulus | 5520 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 216 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 243 to 260 | °C | |
| Mold Temperature | 65.6 to 121 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL EF-6100 | Teknor Apex Company | TPE | Telcar® |
| Stylac™ R340T | Asahi Kasei Chemicals Corporation | AS | Stylac™ |
| DINALON® PA 6 30% CM | Grupo Repol | Nylon 6 | DINALON® |
| Elastron® D D100.A75.N | Elastron USA, Inc. | SBS | Elastron® D |
| Hanwha Total PE E090A | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | EVA | Hanwha Total PE |