LNP™ THERMOCOMP™ KZ001L compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XfVnUe_LNPTHERMOCOMPKZ001Lcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP KZ001L is a compound based on Acetal Copolymer resin containing Glass Fiber. Added features of this material include: Low Extractible. Also known as: LNP* THERMOCOMP* Compound KF-1001 LE M Product reorder name: KZ001L |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 2.0 - 4.0 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.0 - 4.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 2.6 | % | ISO 294-4 |
| Flow direction : 24 hours | 2.9 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2840 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 57.9 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2 |
| Fracture | 54.5 | MPa | ASTM D638 |
| Fracture | 55.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 9.1 | % | ASTM D638 |
| Yield | 9.9 | % | ISO 527-2 |
| Fracture | 27 | % | ASTM D638 |
| Fracture | 43 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| Flexural Stress | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 5.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1300 | J/m | ASTM D4812 |
| 23°C 3 | 84 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.40 | J | ASTM D3763 |
| -- | 1.60 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 156 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 148 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 101 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 93.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR7-7015UR | Spartech Polycom | PC | Spartech |
| Grivory® HT2V-15H | EMS-GRIVORY | Nylon 6T/66 | Grivory® |
| Paracril® CLM | INSA | NBR | Paracril® |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 3105 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Novalloy-S S5230 | PlastxWorld Inc. | PC+ABS | Novalloy-S |