LIHAN® T9706EP
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Nanjing Lihan Chemical Co., Ltd. |
| Trademark: | LIHAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XaIo85_LIHAN-T9706EP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LIHAN® T9706EP is a Polybutylene Terephthalate (PBT) product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 to 1.0 | % | |
| Water Content | 0.40 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2 |
| Flexural Modulus | 9000 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 10 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Melting Temperature | 220 to 225 | °C | DSC |
| CLTE - Flow | 2.0E-5 to 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 250 to 275 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210L | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Sylvin 9469-40D Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Tenopom® POM B3 TZ MF NTLA010 PR333 MSP | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| Hanwha Total PE F120U | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| Wankai WK821 | Zhejiang Wankai New Materials Co., Ltd. | PET | Wankai |