TIPELIN® 7300B
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPELIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XXDV9M_TIPELIN-7300B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPELIN 7300B is a high density bimodal polyethylene copolymer (with butene-1 as comonomer) intended for blow moulding of products with high stiffness and excellent environmental stress crack resistance (ESCR).The grade contains antioxidant and acid scavenger. Applications TIPELIN 7300B is recommended for blow moulding of jerry cans for packaging of aggressive industrial chemicals bounded to UN certificates. The grade is recommended for sheet extrusion as well. It is suitable for corrugated pipes too. TIPELIN 7300B is suitable for food contact and for manufacturing of pharmaceutical packing products. The product complies with Food Contact and Pharmaceutical Regulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.955 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.10 | g/10 min | |
| 190°C/21.6 kg | 12 | g/10 min | |
| 190°C/5.0 kg | 0.40 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, F50) | 1000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 37.0 | MPa | |
| Break, Compression Molded | 36.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield, Compression Molded | 12 | % | |
| Break, Compression Molded | 1400 | % | |
| Flexural Modulus | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 18 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 127 | °C | ISO 306/A120 |
| Oxidation Induction Time (200°C) | 40 | min | EN 728 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 3000-50A | Vi-Chem Corporation | TPE | Sevrene® |
| SOLLAMID A 2700 - A 2730 FV 30 | Krisoll Resinas Plásticas Ltda. | Nylon 66 | SOLLAMID |
| Veroplas GRSJ | PlastxWorld Inc. | SAN | Veroplas |
| Formolon® KVH | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| POCAN® S 7020 000000 | LANXESS GmbH | PBT | POCAN® |