SAXAMID™ 126F4
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dsg9Rm_SAXAMID-126F4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SAXAMID 126F4 is a polyamide 6 injection-molding-grade reinforced with 20 % glass fibres. This product is UL listed. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 150 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7100 | MPa | ISO 527-2/1 |
| Tensile Stress | 148 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5400 | MPa | ISO 178 |
| Flexural Stress 2 | 243 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 49 | kJ/m² | |
| 23°C | 54 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 53 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 207 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 214 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification (1.50 to 1.70 mm) | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GPE2001E-ROHS | S&E Specialty Polymers, LLC | PE, Unspecified | S&E Wire & Cable |
| GAPEX® RPP20EU33AL | Ferro Corporation | PP, Unspecified | GAPEX® |
| LIHAN® A706SH | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |
| Karina BLACK PVC COMPOUND MICRO-EX 4648/1-EXPO (**) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SQUARE® SR8656A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |