RTP ESD C 1780
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XR7haR_RTP-ESD-C-1780.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. ESD C 1780 is modified polyphenylene oxide, PPO, with carbon fiber added for electrical conductivity and excellent static dissipation characteristics. This product is non-sloughing and colorable |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8620 | MPa | ASTM D638 |
| Tensile Strength | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 190 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 98.9 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 93.3 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D955, 0.25in.: 2mil/in.Tensile Elongation, ASTM D638: 1-2%Volume Resistivity, ASTM D257: <10E4 ohm-cmSurface Resistivity, ASTM D257: <10E7 ohm/sqStatic Decay, FTMS-4046.1, Mil B-81705C: pass |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 - 260 | °C | |
| Middle Temperature | 204 - 260 | °C | |
| Front Temperature | 204 - 260 | °C | |
| Mold Temperature | 37.8 - 93.3 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8800 FR2X | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| SILVER® PP 423G10 | Guangdong Silver Age Sci & Tech. Co., Ltd | PP, Unspecified | SILVER® |
| TUFNYL® RGF 25 NATURAL | SRF Ltd. | Nylon 66 | TUFNYL® |
| Boda BDT-LG3701 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Latishield 73/13-07A | LATI S.p.A. | Acetal (POM) Copolymer | Latishield |