Rilsan® ASR 20

Category:	Nylon 12 , Polyamide 12
Manufacturer:	Arkema
Trademark:	Rilsan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	XHplTI_Rilsan-ASR-20.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Rilsan® ASR 20 is a Polyamide 12 (Nylon 12) product filled with filler. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America.

Characteristics include:

Antistatic

Good UV Resistance

Heat Resistant

Mold Release Agent

General Information
Filler / Reinforcement	Filler
Additive	Antistatic Mold Release
Features	Antistatic Good UV Resistance High Heat Resistance
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Density	1100	1100	kg/m³	ISO 1183 ¹
Melt volume-flow rate (235°C/2.16 kg)	5.00	--	cm³/10min	ISO 1133 ²

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile modulus	12600	11400	MPa	ISO 527-2 ³
Tensile Stress (Break)	132	128	MPa	ISO 527-2 ⁴
Tensile Strain (Break)	5.0	4.0	%	ISO 527-2 ⁵

Impact	Dry	Conditioned	Unit	Test Method
Charpy notched impact strength				ISO 179/1eA ⁶
-30°C	10.0	10.0	kJ/m²
23°C	17.0	17.0	kJ/m²
Charpy impact strength				ISO 179/1eU ⁷
-30°C	59.0	58.0	kJ/m²
23°C	59.0	64.0	kJ/m²

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load				ISO 75-2 ⁸
0.45 MPa	175	--	°C
1.8 MPa	160	--	°C
Vicat Softening Temperature (50°C/h, B (50N))	170	--	°C	ISO 306 ⁹
Melting Temperature ¹⁰	178	--	°C	ISO 11357-3 ¹¹
CLTE - Flow	4.0E-5	--	cm/cm/°C	ISO 11359-2 ¹²

Electrical	Dry	Conditioned	Unit	Test Method
Volume resistivity	--	6.0	ohms·m	IEC 60093 ¹³
Comparative tracking index	--	100		IEC 60112 ¹⁴

Flammability	Dry	Conditioned	Unit	Test Method
Burning Behav. at 1.6mm nom. thickn. (1.60 mm)	HB	--		ISO 1210 ¹⁵
Burning Behav. at thickness h (3.20 mm)	HB	--		ISO 1210 ¹⁶

Note Message
1 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
2 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
3 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
4 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
5 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
6 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
7 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
8 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
9 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
10 .	10 °C/min
11 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
12 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
13 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
14 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
15 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
16 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.

Resin Grade	Manufacturer	Category	Trademark
Trexprene® D50CI	Mitsubishi Chemical Performance Polymers, Inc.	TPV	Trexprene®
NYLOY® UB-0010N G35L1N	Nytex Composites Co., Ltd.	Nylon, Unspecified	NYLOY®
APEX® 3603-70NT	Teknor Apex Company	PVC, Flexible	APEX®
Plaslube® PEEK TL15 A	Techmer Engineered Solutions	PEEK	Plaslube®
ICORENE® 9005 Black 9001	A. Schulman Europe	Nylon 12	ICORENE®