Infino NH-1038
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X6gpmG_InfinoNH1038.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino NH-1038 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| natural color | 1.20 | g/cm³ | ASTM D792 |
| natural color | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 22 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.34 - 0.42 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.36 - 0.44 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.36 - 0.44 | % | ISO 2577 |
| Traffic : 3.20mm | 0.34 - 0.42 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 118 | ASTM D785 | |
| R scale | 118 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2100 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 61.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 56.0 | MPa | ASTM D638 |
| Fracture | 57.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 50 | % | ASTM D638 |
| Fracture | 50 | % | ISO 527-2/50 |
| Flexural Modulus 5 | |||
| -- | 2400 | MPa | ASTM D790 |
| -- | 2300 | MPa | ISO 178 |
| Flexural Strength 6 | 86.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 24 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 590 | J/m | ASTM D256 |
| 23°C 8 | 60 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 82.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 82.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 97.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | Thickness: 4mm |
| 8 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo DAP 52-40-40-P | Sumitomo Bakelite North America, Inc. | DAP | Sumitomo DAP |
| Colorite CS Series CS6019GP | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| LNP™ LUBRICOMP™ DX96651 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| PLEXIGLAS® Sheet Resist 65 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |
| OTECH ALLOY OW138 - Cord Jacket | OTECH Corporation | TP, Unspecified | OTECH ALLOY |