OP - PC - Unfilled 68-FDA
| Category: | PC , Polycarbonate |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PC - Unfilled |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X5HlD0_OP---PC---Unfilled-68-FDA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OP-PC-Unfilled 68-FDA is a polycarbonate (PC) material,. This product is available in North America and is processed by injection molding. The main features of OP-PC-Unfilled 68-FDA are:
OP-PC-Unfilled 68-FDA's typical application areas are: food contact applications |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 62.1 | MPa | ASTM D638 |
| Fracture | 72.4 | MPa | ASTM D638 |
| Flexural Modulus | 2310 | MPa | ASTM D790 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 910 | J/m | ASTM D256 |
| Dart Drop Impact | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 138 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 132 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-2 | UL 94 | |
| 3.18 mm | V-2 | UL 94 |
| Additional Information |
|---|
| Melt Mass - Flow Rate (MFR), ASTM D1238, 300°C/1.2kg: 6 to 9 g/10 min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 118 - 124 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 288 - 310 | °C | |
| Middle Temperature | 299 - 321 | °C | |
| Front Temperature | 310 - 332 | °C | |
| Processing (Melt) Temp | 316 - 343 | °C | |
| Mold Temperature | 82.2 - 116 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF6AAF (Series: FC/HE/tl) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Anjacom® 155-GF50 | Almaak International GmbH | PC | Anjacom® |
| Diamond ABS 3501 GF-30 | Network Polymers, Inc. | ABS | Diamond ABS |
| DURAFIDE® 6565A7 | Polyplastics Co., Ltd. | PPS | DURAFIDE® |
| LNP™ THERMOCOMP™ WX15003 compound | SABIC Innovative Plastics Europe | PBT | LNP™ THERMOCOMP™ |