LNP™ LUBRICOMP™ Cycoloy_C2801 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WYGWKk_LNPLUBRICOMPCycoloyC2801compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 5% PTFE reinforced PC+ABS wear resistant flame retardant resin for moving components in business equipment. Medium heat performance |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.40 - 0.50 | % | Internal method |
| Transverse flow : 3.20mm | 0.30 - 0.50 | % | Internal method |
| K (wear) Factor 1 | 430 | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 62.1 | MPa | ASTM D638 |
| Fracture | 51.7 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 110 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 2720 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 95.1 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.21 | ASTM D1894 | |
| With steel-static | 0.16 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 82.2 | °C | ASTM D648 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.49 mm | 5VB | UL 94 |
| Note Message | |
|---|---|
| 1 . | xE-10, PV=2000 psi-fpm vs Steel |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE CC1053 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Scolefin 42 T 23-0 | Ravago Group | PP Copolymer | Scolefin |
| Generic PPE+PS+Nylon - Glass Fiber | Generic | PPE+PS+Nylon | Generic |
| Epoxies, Ect. 60-7156 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Karina CLEAR PVC COMPOUND 800-204-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |