WPP PP PRC25GF3-Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HS5fEo_WPP-PP-PRC25GF3-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PRC25GF3-Black is a polypropylene homopolymer (PP Homopoly) product, which contains a 30% glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. WPP PRC25GF3-Black applications include the automotive industry and consumer goods. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 78.0 | MPa | ASTM D638 |
| Yield 2 | 84.0 | MPa | ASTM D638 |
| Yield | 79.0 | MPa | ISO 527-2/5 |
| Yield | 86.0 | MPa | ISO 527-2/50 |
| Tensile Elongation 3(Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | |||
| -- 4 | 4900 | MPa | ASTM D790 |
| Secant 5 | 5100 | MPa | ASTM D790 |
| -- 6 | 5200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.5 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 94 | J/m | ASTM D256 |
| -40°C | 6.5 | kJ/m² | ISO 180 |
| 23°C | 9.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 610 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 158 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 157 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 147 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 146 | °C | ISO 75-2/A |
| 1.8 MPa, not annealed | 141 | °C | ISO 75-2/Af |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted. |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® HJ4045 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Daicel PP PNAS2 (Type A) | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Hanwha Total PP FB51 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| POLYCOMPO PE 3550R | POLYCOMPO Co.,Ltd. | LLDPE | POLYCOMPO PE |
| CYCOLOY™ XCY620 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |