Order Products : sales@su-jiao.com

KPOL-PP K-PPC 8.0

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	WBdrBu_KPOL-PP-K-PPC-8-0.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene Heterophasic Copolymer

Applications

Injection Molding, Automobile Applications, Battery case ; Toys; Household Appliances; Crates; Buckets; Base resin for compounding ; High impact resistance parts.

It exhibits a good fluidity combined with a good balance of impact and stiffness as well as a low warpage tendency. Even at sub-zero temperatures and also provides good surface properties and excellent processability.

Characteristics

The KPOL® resin is a propylene impact copolymer designed for injection molding applications, has excellent toughness and good dimensional stabilityIt is a controlled rheology grade.

General Information
Additive	Antioxidant Nucleating Agent
Features	Antioxidant Controlled Rheology Food Contact Acceptable Good Dimensional Stability Good Flow Good Processability Good Stiffness Good Toughness High Impact Resistance Impact Copolymer Low Warpage Nucleated
Uses	Appliances Automotive Applications Battery Cases Compounding Crates Pails Toys
Agency Ratings	FDA 21 CFR 177.1520
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	8.0	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale, Compression Molded)	65		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, Compression Molded)	26.0	MPa	ASTM D638
Tensile Elongation ²(Break, Compression Molded)	8.0	%	ASTM D638
Flexural Modulus - 1% Secant (Compression Molded)	1100	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (20°C, Compression Molded)	60	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded)	93.0	°C	ASTM D648
Vicat Softening Temperature	148	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X3602	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
RTP 2299 X 115088 C	RTP Company	PEEK	RTP
CONTINUUM™ DGDA-2502 NT	The Dow Chemical Company	HDPE	CONTINUUM™
Generic Nylon 1212	Generic	Nylon 1212	Generic
LEXAN™ EXL1810T resin	SABIC Innovative Plastics	PC	LEXAN™