Ultradur® B 4300 G4 BK5110
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W2qRA3_Ultradur-B-4300-G4-BK5110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultradur B 4300 G4 BK5110 is an easy flowing, pigmented black, injection molding PBT with 20% glass fiber reinforcement for rigid, tough, and dimensionally stable parts. Applications Typical applications include car door handles, housings for small electric motors, headlight retainers and drum controllers. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.20 | % | |
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number (Reduced Viscosity) | 110.0 | ml/g | ISO 1628 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 107 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 199 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 223 | °C | ISO 3146 |
| RTI Elec | UL 746 | ||
| 0.750 mm | 130 | °C | |
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 0.750 mm | 125 | °C | |
| 1.50 mm | 125 | °C | |
| 3.00 mm | 125 | °C | |
| RTI Str | UL 746 | ||
| 0.750 mm | 130 | °C | |
| 1.50 mm | 130 | °C | |
| 3.00 mm | 140 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | < 1.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PSH 6132 | Marco Polo International, Inc. | PS (HIPS) | MARPOL® PSH |
| TAROLOX 111 G6 Y0 | Taro Plast S.p.A. | PET | TAROLOX |
| TPX® MX004 | Mitsui Chemicals America, Inc. | PMP Copolymer | TPX® |
| Hifax DKG726P | LyondellBasell Industries | TPO (POE) | Hifax |
| INSTRUC PA610GF30 | Infinity LTL Engineered Compounds | Nylon 610 | INSTRUC |