Yuyao PPO GFN2-701
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Yuyao Tenglong Plastics Co., Ltd. |
| Trademark: | Yuyao PPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VxpkhM_Yuyao-PPO-GFN2-701.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Yuyao PPO GFN2-701 is a Polyphenylene Ether + PS (PPE+PS) product filled with glass fiber. It can be processed by injection molding and is available in Asia Pacific. Typical application: Engineering/Industrial Parts. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 5500 | MPa | ASTM D790 |
| Flexural Strength | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) | 8.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 130 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.3E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Weifang Kingdom CPE135A | Weifang Kingdom Plastic Co., Ltd | CPE | Weifang Kingdom |
| ASTATAL™ FV30 | Marplex Australia Pty. Ltd. | Acetal (POM) Homopolymer | ASTATAL™ |
| Hostacom EKC 330N E1 G62514 | LyondellBasell Industries | PP Copolymer | Hostacom |
| OTECH ALLOY OM6018-Boot | OTECH Corporation | TP, Unspecified | OTECH ALLOY |
| Metocene MF650Y | LyondellBasell Industries | PP Homopolymer | Metocene |