Eltex® PF6812AA
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | Eltex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VWIpDD_EltexPF6812AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELTEX® PF6812AA is a metallocene LLDPE resin produced in Europe Benefits & Features ELTEX® PF6812AA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:
ELTEX® PF6812AA is formulated with antioxidants. Applications ELTEX® PF6812AA has been developed for use in coextruded blown film structures particularly suitable for food packaging, hygiene or industrial applications. Its unique balance between stiffness, toughness and optical properties makes it the material of choice for the most advanced film compositions with an optimum thickness reduction. Its excellent resistance to slow crack growth also makes ELTEX® PF6812AA valuable for geomembrane applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.932 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 1184 | ||
| 1% secant, MD : 25 µm, blown film | 350 | MPa | ISO 1184 |
| 1% secant, TD : 25 µm, blown film | 410 | MPa | ISO 1184 |
| Tensile Stress | ISO 1184 | ||
| MD : Yield, 25 µm, blown film | 17.0 | MPa | ISO 1184 |
| TD : Yield, 25 µm, blown film | 19.0 | MPa | ISO 1184 |
| MD : Broken, 25 µm, blown film | 60.0 | MPa | ISO 1184 |
| TD : Broken, 25 µm, blown film | 55.0 | MPa | ISO 1184 |
| Tensile Elongation | ISO 1184 | ||
| MD : Broken, 25 µm, blown film | 640 | % | ISO 1184 |
| TD : Broken, 25 µm, blown film | 770 | % | ISO 1184 |
| Dart Drop Impact (25 µm, Blown Film) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 70 | g | ASTM D1922 |
| TD : 25 µm, blown film | 520 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 65 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 9.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3284 | RTP Company | ETFE | RTP |
| SLOVAMID® 66 GF 30 FRA 5 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Dynaprene® SE0028A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Keltan® 6950C | LANXESS Buna GmbH | EPDM | Keltan® |
| HK GPPS N1841H | Hong Kong Petrochemical Co. Ltd. | PS (GPPS) | HK GPPS |