Baypreg® F 310 (25 mm Glass Mat Reinforced Sandwich)

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	Covestro - PUR
Trademark:	Baypreg®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	sYS7ZZ_Baypreg-F-310-25-mm-Glass-Mat-Reinforced-Sandwich-.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Baypreg F 310 system is a two component polyurethane system used in compression molding of fiber-reinforced sandwich panels to produce a variety of automotive parts. Some identified applications include door panels, sunshades, spare tire covers, load floors, etc. The Baypreg F 310 system provides lightweight alternatives to ABS, PP, SMC, and wood products while demonstrating very high flexural stiffness and excellent thermal properties. Baypreg F 310 system offers very diverse properties over a wide range of part thicknesses and densities while still providing cost effective substrate parts when combined with reinforcing materials. As with any product, use of the Baypreg F 310 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 50% filler by weight
Uses	Application in Automobile Field
Forms	Liquid
Processing Method	Compression molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.128	g/cm³	ASTM D792

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus (22°C)	2750	MPa	ASTM D790
Flexural Strength (22°C)	7.00	MPa	ASTM D790

Thermoset	Nominal Value
Thermoset Components
Component a	Mixing ratio by weight: 100
Component B	Mixing ratio by weight: 180

Additional Information
Part A Type: Isocyanate Appearance: Dark Brown Liquid Specific Gravity @ 25°C: 1.21 Viscosity @25°C: 350 mPa Flash Point, PMCC: 223°C NCO: 28.5 wt% Part B Type: Polyol Appearance: Black liquid Specific Gravity @ 25°C: 1.083 Viscosity @25°C: 1380 mPa-s Flash Point, PMCC: 166°C Hydroxyl Number: 610 Reinforcing Mat Weight: 600 g/m³Tricel Honeycomb (untreated): 25 mmMolded Thickness: 25 mmChemical Temperature: 21 to 27°CMold Temperature: 100 to 120°CCure Time: 65 to 90 secTime from Spray to Mold Close: 75 secNucleation (resin): Up to 40% or as neededDegassing, if necessary: Open tool at 17 sec for 5 sec

Additional Information

Part A Type: Isocyanate Appearance: Dark Brown Liquid Specific Gravity @ 25°C: 1.21 Viscosity @25°C: 350 mPa Flash Point, PMCC: 223°C NCO: 28.5 wt% Part B Type: Polyol Appearance: Black liquid Specific Gravity @ 25°C: 1.083 Viscosity @25°C: 1380 mPa-s Flash Point, PMCC: 166°C Hydroxyl Number: 610 Reinforcing Mat Weight: 600 g/m³Tricel Honeycomb (untreated): 25 mmMolded Thickness: 25 mmChemical Temperature: 21 to 27°CMold Temperature: 100 to 120°CCure Time: 65 to 90 secTime from Spray to Mold Close: 75 secNucleation (resin): Up to 40% or as neededDegassing, if necessary: Open tool at 17 sec for 5 sec

Resin Grade	Manufacturer	Category	Trademark
TECHLEN ST920S	DAEHA Co., LTD	PP, Unspecified	TECHLEN
TAIRIPRO K4515	Formosa Plastics Corporation	PP Random Copolymer	TAIRIPRO
Arak HDPE BL6	Shazand (Arak) Petrochemical Corporation	HDPE	Arak HDPE
Di-Pak™ E-4566	Hapco Inc.	TP, Unspecified	Di-Pak™
Karina GREEN PVC COMPOUND 650-40/57 (MP-1.0) (*)	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina