| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VUM9aT_RTP-200-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 200 UV is a UV stabilized nylon 6/6 general purpose resin. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 | -- | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.2 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | 110 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 82.7 | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | 30 | % | ASTM D638 |
| Flexural Modulus | 2900 | 1310 | MPa | ASTM D790 |
| Flexural Strength | 117 | 41.4 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 800 J/m | No Break | ASTM D4812 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 232 | 221 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 90.6 | 71.1 | °C | ASTM D648 |
| CLTE - Flow | 7.2E-5 | -- | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.25 | -- | W/m/K | ASTM C177 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.70 | 4.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.10 | ASTM D150 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| -- | -- | V-2 | UL 94 | |
| 1.59 mm | V-2 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 The value listed as Flammability, UL 94, was tested in accordance with RTP test standards. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 274 - 288 | °C | |
| Middle Temperature | 274 - 288 | °C | |
| Front Temperature | 274 - 288 | °C | |
| Mold Temperature | 65.6 - 107 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3545 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| NYCOA Polyamide ASN 27 440 KNF | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Durepol® PBT A3 V20 CNZ0350 BT331 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| INTEGRATE™ NP507030 | LyondellBasell Industries | Polyolefin, Unspecified | INTEGRATE™ |
| SPESIN® KP210 | Kolon Plastics, Inc. | PBT | SPESIN® |