SOLLAMID B 2700 FV 30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Krisoll Resinas Plásticas Ltda. |
| Trademark: | SOLLAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VQvZis_SOLLAMID-B-2700-FV-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SOLLAMID B 2700 FV 30 is a Polyamide 6 (Nylon 6) material filled with 30% glass fiber. It is available in Latin America. Primary attribute of SOLLAMID B 2700 FV 30: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.35 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.40 | -- | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.95 | -- | % | ASTM D570 |
| Heat Stability | 100 to 110 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 122 | 110 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8000 | 5000 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 160 | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | 4.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8000 | 4500 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 240 | 140 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 12 | 20 | kJ/m² | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 210 | -- | °C | |
| 1.8 MPa, Unannealed | 200 | -- | °C | |
| Melting Temperature | 214 to 220 | -- | °C | |
| CLTE - Flow | 2.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | Notch B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aaroprene® ATPR 2000 60A | Aaron Industries Corp. | TPE | Aaroprene® |
| Borealis PP RC101 | Borealis AG | PP, Unspecified | Borealis PP |
| Flexalloy® OR 9800-60 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| Karina CLEAR PVC COMPOUND 75/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina CLEAR PVC COMPOUND -E 75/161-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |