EXPLORE® XP9003
| Category: | PC , Polycarbonate |
| Manufacturer: | Matrix Polymers |
| Trademark: | EXPLORE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VKTCR7_EXPLORE-XP9003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Explore XP9003 is a rotomouldable Polycarbonate powder. It's low viscosity make it an ideal grade for applications where good aestetic properties are more important than impact strength. This material will conform to the UL94 V-2 fame retardancy test, is very rigid and very hard, and is available in clear or coloured forms. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 23.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 90 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ARM Impact (-40°C, 3.00 mm) | 22.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 130 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxiglas® MG820 | Maxiglas Corporation | Acrylic (PMMA) | Maxiglas® |
| Sylvin 8853-70 White 1423 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vipel® K190-RTM-17 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Borealis PP VG621 | Borealis AG | TPO | Borealis PP |
| EPO-TEK® OG133-8 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |