Bergamid™ B70 G30 grey VN7445CF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VHCSkU_Bergamid-B70-G30-grey-VN7445CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bergamid™ B70 G30 grey VN7445CF is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity 1 | 1.35 | -- | g/cm³ | DIN 53479 |
| Molding Shrinkage - Flow 2(23°C, 4000 mm) | 0.10 to 0.60 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 7800 | 6000 | MPa | ISO 527-2/1 |
| Tensile Strength 3(23°C, 4.00 mm) | 120 | 100 | MPa | ISO 527 |
| Tensile Elongation 4(Break, 23°C, 4.00 mm) | 2.0 | 3.5 | % | ISO 527 |
| Flexural Modulus (23°C) | 7000 | -- | MPa | ISO 178 |
| Flexural Stress (23°C) | 175 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 6.0 | 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | 48 | > 60 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | 210 | -- | °C | ISO 75-2/C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 to 3.00 mm, ALL) | HB | HB | Internal Method |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | ±0.03 |
| 2 . | Bergmann method |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer SG8 | Shanghai Potomer International Trade Co., Ltd. | PVC, Rigid | Shanghai Potomer |
| Accura® Peak™ | 3D Systems | Epoxy | Accura® |
| Indothene LL 20FS010 | Reliance Industries Limited | LLDPE | Indothene LL |
| KOPA® KN333G30 | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| EPAMOULD 760D15 | Epaflex Polyurethanes S.R.L. | TPU-Polyether | EPAMOULD |