Lotryl® 20MA08
| Category: | EMA , Ethylene Methyl Acrylate Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Lotryl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VFVE5E_Lotryl-20MA08.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LOTRYL® 20MA08 is a random copolymer of Ethylene and Methyl Acrylate produced by high-pressure radicalar polymerization process. Applications Due to the methyl acrylate content, LOTRYL® 20MA08 can be used for applications where softness, flexibility and polarity are required. Typical applications are extrusion coating, coextrusion and compounds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 to 9.0 | g/10 min | ASTM D1238, ISO 1133 |
| Methyl Acrylate Content | 18.0 to 22.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 83 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 9.00 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | 800 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (Compression Molded) | 20.0 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 46.0 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 76.0 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 to 170 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Die Temperature | 170 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 6740/40 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| Surlyn® PC350 | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| NORYL GTX™ GTX6203 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS+Nylon | NORYL GTX™ |
| Delrin® 510GR NC000 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Fainplast PVC GS 4510/R | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |