INSTRUC PSUGF20
| Category: | PSU , Polysulfone |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INSTRUC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V7K1yM_INSTRUC-PSUGF20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% GLASS FIBER REINFORCED POLYSULFONE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus | 5520 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact | 530 to 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 185 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 316 to 338 | °C | |
| Middle Temperature | 299 to 327 | °C | |
| Front Temperature | 299 to 327 | °C | |
| Processing (Melt) Temp | 338 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN2320SB | Ginar Technology Co., LTD. | Nylon 66/6 | Mapex |
| Moplen HP502N | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Axiall PVC 8552 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Moplen HP640RK | LyondellBasell Industries | PP Homopolymer | Moplen |
| Sylvin 8394-90C Natural | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |