RTP 1402 N L
| Category: | PESU , Polyethersulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V5oroE_RTP-1402-N-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5860 | MPa | ASTM D638 |
| Tensile Strength | 121 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 4960 | MPa | ASTM D790 |
| Flexural Strength | 176 | MPa | ASTM D790 |
| Compressive Strength | 124 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 590 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 207 | °C | ASTM D648 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.29 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | ASTM D150 | |
| Arc Resistance | 70.0 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as UL-94, was tested in accordance with RTP Company tests. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 343 - 399 | °C | |
| Middle Temperature | 343 - 399 | °C | |
| Front Temperature | 343 - 399 | °C | |
| Mold Temperature | 93.3 - 177 | °C | |
| Injection Pressure | 68.9 - 124 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M2101R (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| Yanshan PE LD100BW | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Lotryl® BESTPEEL 2012 | Arkema | EMA | Lotryl® |
| Optix® CA-81 FDA | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |
| LNP™ STAT-KON™ DD0009 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |