LNP™ LUBRICOMP™ KFL36 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3D42Oh_LNP-LUBRICOMP-KFL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KFL36 is a compound based on Acetal Copolymer resin containing 30% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KFL-4036 Product reorder name: KFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 to 1.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.16 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.26 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10800 | MPa | ASTM D638 |
| -- | 10600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 88.0 | MPa | ASTM D638 |
| Break | 84.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.3 | % | ASTM D638 |
| Break | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 9280 | MPa | ASTM D790 |
| -- 5 | 9930 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 130 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 107 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.40 | ||
| vs. Itself - Static | 0.46 | ||
| Wear Factor - Washer | 235 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 50 | J/m | ASTM D256 |
| 23°C 7 | 5.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 8(23°C) | 25 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 10.3 | J | ASTM D3763 |
| -- | 2.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 183 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 163 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 161 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 161 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 9.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fiberfil® J-60/30/E5 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Hanwha Total PP HJ730 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| PARAPET GR01270 | Kuraray Co., Ltd. | Acrylic (PMMA) | PARAPET |
| POLYfill PPC T25020 UV | Polykemi AB | PP Copolymer | POLYfill |
| SQUARE® SSR2033-30MA/MB | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |