TECAST™ 6PAG Datasheet,Nylon 6,Ensinger Inc.-SHANGHAI SUSHENG

TECAST™ 6PAG

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Ensinger Inc.
Trademark:	TECAST™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	UtrsiA_TECAST-6PAG.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
TECAST™ cast nylon, available in a variety of grades, offers a combination of good mechanical properties, excellent bearing and wear characteristics, and the large-size capabilities of the casting process. Its fatigue resistance, noise damping ability, corrosion resistance, and light weight make TECAST™ ideal for metal replacement applications, such as bearings, gears, sheaves, and sprockets. At one-eighth the weight of bronze, TECAST™ is easier to handle and maintain than metals such as iron, aluminum, brass, and bronze, which it typically replaces in industrial wear applications. Other materials that TECAST™ commonly replaces because of its superior performance are laminated phenolics, elastomers, and wood. TECAST™ has excellent wear and abrasion resistance, resulting in extended component life and lower maintenance cost. Its formulations are readily available in rod, plate, and tube. Nonstandard shapes, such as rings, discs, and blocks can be economically produced in small quantities with short lead times. Custom parts can be cast-to-size or near-net-shape with relatively inexpensive tooling. Its unique combination of strength, wear resistance, toughness, machinability, and corrosion resistance make TECAST™ cast nylon ideal for bearings, thrust washers, bushings, wear pads, sheaves, rollers, gears, sprockets, and wheels. TECAST™ is commonly used in construction equipment, material handling systems, amusement park rides, pulp and paper processing equipment, steel mills and industrial equipment. A graphite powder-filled cast type 6 nylon with properties similar to 6PAM but better suited to wet applications.

Message

TECAST™ cast nylon, available in a variety of grades, offers a combination of good mechanical properties, excellent bearing and wear characteristics, and the large-size capabilities of the casting process. Its fatigue resistance, noise damping ability, corrosion resistance, and light weight make TECAST™ ideal for metal replacement applications, such as bearings, gears, sheaves, and sprockets. At one-eighth the weight of bronze, TECAST™ is easier to handle and maintain than metals such as iron, aluminum, brass, and bronze, which it typically replaces in industrial wear applications. Other materials that TECAST™ commonly replaces because of its superior performance are laminated phenolics, elastomers, and wood. TECAST™ has excellent wear and abrasion resistance, resulting in extended component life and lower maintenance cost. Its formulations are readily available in rod, plate, and tube. Nonstandard shapes, such as rings, discs, and blocks can be economically produced in small quantities with short lead times. Custom parts can be cast-to-size or near-net-shape with relatively inexpensive tooling.

Its unique combination of strength, wear resistance, toughness, machinability, and corrosion resistance make TECAST™ cast nylon ideal for bearings, thrust washers, bushings, wear pads, sheaves, rollers, gears, sprockets, and wheels. TECAST™ is commonly used in construction equipment, material handling systems, amusement park rides, pulp and paper processing equipment, steel mills and industrial equipment.

A graphite powder-filled cast type 6 nylon with properties similar to 6PAM but better suited to wet applications.

General Information
Filler / Reinforcement	Graphite fiber reinforced material
Features	Noise reduction Machinable Good corrosion resistance Good wear resistance Good wear resistance Fatigue resistance Good toughness
Uses	Wheels Bushing Gear Industrial application Roller Architectural application field Metal substitution Thrust washer Bearing
Forms	Plate Bar Pipe

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.15 - 1.17	g/cm³	ASTM D792
Water Absorption (23°C, 24 hr)	1.2	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale, 23°C)	115		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2410	MPa	ASTM D638
Tensile Strength (Yield, 23°C)	75.8	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	20	%	ASTM D638
Flexural Modulus (23°C)	2410	MPa	ASTM D790
Flexural Strength (23°C)	86.2	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Unnotched Izod Impact (23°C)	32	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, not annealed	188	°C	ASTM D648
1.8 MPa, not annealed	93.3	°C	ASTM D648
Melting Temperature	220	°C	ASTM D2133
CLTE - Flow	7.2E-5	cm/cm/°C	ASTM D696
Maximum Service Temperature
Intermittent	149	°C
Long Term	93	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	20	kV/mm	ASTM D149
Dielectric Constant ¹(23°C, 60 Hz)	3.70		ASTM D150

Additional Information
Data obtained from extruded shapes material.

Note Message
1 .	50% RH

Resin Grade	Manufacturer	Category	Trademark
SIMONA® SIMOPOR-COLOR	SIMONA AMERICA, Inc.	PVC, Unspecified	SIMONA®
Silamid® L	Roonamid a.s.	Nylon 6	Silamid®
SumiDurez 156	SumiDurez Singapore Pte Ltd	Phenolic	SumiDurez
Generic Acetal (POM) Copolymer+PE	Generic	Acetal (POM) Copolymer+PE	Generic
Hoegolup® AIM blue 5117	HP-T Höglmeier Polymer-Tech GmbH & Co. KG	HDPE	Hoegolup®