Polychim HV22XF
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polychim Industrie S.A.S. |
| Trademark: | Polychim |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UpxXW3_PolychimHV22XF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
APPLICATIONS :
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 - 6.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 38.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 8.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3 | < 1550 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 36 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 106 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 55.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525 4 |
| -- | 96.0 | °C | ASTM D1525 5 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | < 0.0 | YI | DIN 6167 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 速率 A (50°C/h), 压 力1 (10N) |
| 5 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AF30BK6030 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Mylar® WC (500 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Nylfor® R 66 CM/15 E8 UV GREY 7102 | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| Huafon JF-W-D6030 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| TOTAL Polypropylene PPC 4740WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |