Order Products : sales@su-jiao.com
POCAN® DP CF 2200 000000
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UgW6AQ_POCAN-DP-CF-2200-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT+PC, non-reinforced, injection molding, flame retardant, improved impact strength, low tendency to warp |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.31 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 250°C, 2.00 mm 1 | 0.90 | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.50 | % | |
| Flow : 250°C, 2.00 mm 3 | 0.90 | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 104 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 2.9 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 15 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 2500 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | ||
| 3.5% Strain, 23°C | 70.0 | MPa | |
| 23°C 6 | 75.0 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 5.0 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT+PC, GFHLMPR, 09-020; ISO1043-(PBT+PC) FR (17) | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Admissible Residence Time at Tmax | < 5.0 | min | |
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 170 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | |
| 0°C | 11 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 150 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 118 | °C | ISO 306/B120 |
| Ball Pressure Test (115°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 8.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.30 | ||
| 23°C, 1 MHz | 2.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 0.025 | ||
| 23°C, 1 MHz | 0.014 | ||
| Comparative Tracking Index (Solution A) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 800 | °C | |
| 1.60 mm | 800 | °C | |
| 3.00 mm | 800 | °C |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 60°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 60°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® C CTA | Nanjing Julong Engineering Plastics Co., LTD | PC+PBT | Wondel® C |
| Delta N66-100A L | Delta Polymers | Nylon 66 | Delta |
| Ecomass® 4703ZC76 | Ecomass Technologies | TPU, Unspecified | Ecomass® |
| LNP™ STAT-LOY™ NX13401 compound | SABIC Innovative Plastics | PC+ABS | LNP™ STAT-LOY™ |
| LubriOne™ LB 6600-5011 RS Natural | PolyOne Corporation | Nylon 66 | LubriOne™ |