AVIMID® RB

Category:	PI, TS , Thermoset Polyimide
Manufacturer:	Cytec Industries Inc.
Trademark:	AVIMID®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	FQ5nTo_AVIMID-RB.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
AVIMID® RB is a high temperature, 644°F (340°C) Tg thermoset polyimide resin with wet service capability to more than 530°F (277°C) and dry service capability of 600°F (316°C). AVIMID RB has excellent thermal oxidative stability and resistance to aircraft fluids. AVIMID RB was formulated for prepreg autoclave vacuum bag processing, but can be successfully compression molded both as a prepreg and in dry forms as neat resin or chopped-fiber molding compound. Unidirectional tape and woven prepreg of AVIMID RB will retain their tack and drape for 14 days at 70°F (21°C). Standard autoclave or compression molding processes, to a final temperature of 680°F (360°C) will result in full Tg development/cure with no need for post-cure treatment. AVIMID RB can be solution impregnated on a variety of fibers and fabrics.

Message

AVIMID® RB is a high temperature, 644°F (340°C) Tg thermoset polyimide resin with wet service capability to more than 530°F (277°C) and dry service capability of 600°F (316°C). AVIMID RB has excellent thermal oxidative stability and resistance to aircraft fluids.

AVIMID RB was formulated for prepreg autoclave vacuum bag processing, but can be successfully compression molded both as a prepreg and in dry forms as neat resin or chopped-fiber molding compound. Unidirectional tape and woven prepreg of AVIMID RB will retain their tack and drape for 14 days at 70°F (21°C).

Standard autoclave or compression molding processes, to a final temperature of 680°F (360°C) will result in full Tg development/cure with no need for post-cure treatment. AVIMID RB can be solution impregnated on a variety of fibers and fabrics.

General Information
Features	Autoclavable Good Thermal Aging Resistance Heat Cure High Heat Resistance Oxidation Resistant
Uses	Aerospace Applications Structural Parts
Forms	Fabric Fiber
Processing Method	Compression Molding Vacuum Forming

Mechanical	Nominal Value	Unit
Tensile Modulus ¹	3790	MPa
Tensile Strength ²	82.7	MPa
Tensile Elongation (Break)	2.4	%
Flexural Modulus	3790	MPa
Flexural Strength	111	MPa

Note Message
1 .	Neat resin
2 .	Neat resin

Resin Grade	Manufacturer	Category	Trademark
Prixene® EL010E20S	POLYMAT	LLDPE	Prixene®
SABIC® STAMAX 60YM241	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® STAMAX
ColorRx® PET-1000RX	LTL Color Compounders, Inc.	PET	ColorRx®
Daelim Po1y® LH-402	DAELIM INDUSTRIAL CO., LTD.	HDPE	Daelim Po1y®
3M™ Dyneon™ Fluoroelastomer FPO 3741	3M Advanced Materials Division	Fluorelastomer	3M™ Dyneon™ Fluoroelastomer