NYCOA Polyamide 2326 HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UXlREy_NYCOA-Polyamide-2326-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 2326 HS is an impact modified, heat stabilized nylon 6 resin, which offers outstanding toughness, impact strength and chemical resistance. This material is specially formulated to give a high degree of impact strength, without the loss of stiffness and rigidity. NYCOA 2326 HS processes easily on conventional injection molding and extrusion equipement. Typical applications include clips, fasteners, wiring harnesses, power tool housings, and connectors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.4 | % | ASTM D955 |
| Transverse flow | 1.6 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.7 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 45.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 130 | % | ASTM D638 |
| Flexural Modulus 3 | 1500 | MPa | ASTM D790 |
| Flexural Strength 4 | 58.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 880 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 140 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 48.9 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 221 - 241 | °C | |
| Middle Temperature | 235 - 252 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 254 - 266 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.517 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 5440 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| Radilon® A RV300L 333 NER | Radici Plastics | Nylon 66 | Radilon® |
| NEFTEKHIM PE 4441R (40404) | Nizhnekamskneftekhim Inc. | MDPE | NEFTEKHIM PE |
| FRblend® PP-1501 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP, Unspecified | FRblend® |
| ESPRENE EPDM 601F | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |