LITEN FL 20
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | UNIPETROL RPA |
| Trademark: | LITEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UHeuT4_LITEN-FL-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LITEN FL 20 is a copolymer with medium density, broad molecular weight distribution and UV stabilization. It can be used for manufacture of fine packaging films of recommended minimal thickness of 10 µm. Its stabilization system provides a lifetime of 2 years (central European climate) for 120 µm) film. The grade enables manufacture of soft films even at thicknesses of (30 - 50) µm. LITEN FL 20 is also suitable for modification of PE-LD film grades; the modified films exhibit improved mechanical properties at lower thickness. The recommended FL 20 content in PE-LD film is (10 - 30) %. Liten FL 20 meets the hygienic requirements on materials and articles intended for contact with foodstuffs according to Regulation (EC) 1935/2004 of the European Parliament and of the Council, as well as according to Commission Regulation (EU) No 10/2011 including changes and additions. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.20 | g/10 min | |
| 190°C/21.6 kg | 20 | g/10 min | |
| 190°C/5.0 kg | 1.0 | g/10 min | |
| Environmental Stress-Cracking Resistance (50°C, 100% Detergent, F50) | 350 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 56 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 17.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2 |
| Flexural Modulus | 600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 14 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 114 | °C | ISO 306 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 9712 | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| Topolymer® 8211-P | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Unichem 9904-03 | Colorite Polymers | PVC, Unspecified | Unichem |
| Evoprene™ GC 5690 | AlphaGary | SEBS | Evoprene™ GC |
| Formolene® 2502A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |