Epoxies, Ect. 20-2523
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Epoxies, Etc. |
| Trademark: | Epoxies, Ect. |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UF0kWt_Epoxies-Ect-20-2523.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
20-2523 is a high performance two component urethane system. This easy to use polyurethane is very low in viscosity and ideal for potting or encapsulating delicate electronic components. 20-2523 exhibits very low shrinkage, stress, and exotherm throughout the cure cycle. This system is also well known for its outstanding thermal shock and excellent dielectric properties. 20-2523 is ideal for potting applications where a wide operating temperature (-55 to +130°C) is required. It is also a good choice when exposure to salt water, mild acids and bases, and aliphatic hydrocarbons is expected. Features:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.59 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 1.6E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Resistivity | 1.5E+13 | ohms |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity (25°C) | 2950 | cP |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Operating Temperature | -55.0 to 130 | °C | |
| Thermal Shock 1(-65 to 130°C) | Pass |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | Black | ||
| Mix Ratio by Weight (PBW) | |||
| Part A | 100 | ||
| Part B | 20 | ||
| Mix Ratio by Volume (PBV) | |||
| Part A | 100 | ||
| Part B | 23 | ||
| Density | |||
| 25°C 2 | 1.23 | g/cm³ | |
| 25°C 3 | 1.46 | g/cm³ | |
| Viscosity | |||
| 25°C 4 | 0.20 | Pa·s | |
| 25°C 5 | 6.0 | Pa·s | |
| Curing Time | |||
| 85°C | 0.66 | hr | |
| 65°C | 1.5 | hr | |
| 45°C | 2.5 | hr | |
| 25°C | 24 | hr | |
| Pot Life 6(25°C) | 75 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Water Absorption | |||
| -- 7 | 0.15 | % | |
| -- 8 | 0.44 | % | |
| Shore Hardness (Shore D) | 50 | ||
| Tensile Strength | 11.0 | MPa | |
| Tensile Elongation at Break | 50 | % | |
| Electric Strength | 25 | kV/mm | |
| Relative Permittivity (100 Hz) | 4.70 | ||
| Volume Resistivity | 3.4E+13 | ohms·cm | |
| Dissipation Factor (100 Hz) | 0.090 |
| Note Message | |
|---|---|
| 1 . | 10 cycles |
| 2 . | Part B |
| 3 . | Part A |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 1 lb. mass |
| 7 . | After 24 hours |
| 8 . | After 7 days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2635A | Teknor Apex Company | TPE | Telcar® |
| Sinpolene MBB1402 | Teknor Apex Asia Pacific PTE. LTD. | LDPE | Sinpolene |
| Axiall PVC HH-6730 | Axiall Corporation | PVC Alloy | Axiall PVC |
| Kepital® TE-23(FU2015) | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| KRALASTIC® ST-100 | Nippon A&L Inc. | ABS | KRALASTIC® |