Menzolit® BMC 1500
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U6eX4t_Menzolit-BMC-1500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® BMC 1500 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® BMC 1500 is a special BMC for the use at elevated temperature. The glass content is set to a level that combines good flowability with good strength and stiffness properties. Even without a specific fire retardant the fire retardancy HB according to UL 94 is achieved. Typical applications are functional components, housings and covers for kitchen ware, iron handels and similar equipment within the household and appliances industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.00 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- | 0.30 | % | ISO 2577 |
| -- 1 | 0.0 | % | DIN 53464 |
| Water Absorption (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 14000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 32.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 11000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 24 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 150 | °C | ISO 75-2/A |
| Continuous Use Temperature | 190 | °C | Internal Method |
| Glass Transition Temperature | 185 | °C | DSC |
| CLTE - Flow | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 22 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Glow Bar | Level BH 2 <= 95 | IEC 60707-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 150 | °C | |
| Injection Pressure | 2.00 to 8.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ColorFast® PC200 | LTL Color Compounders, Inc. | PC | ColorFast® |
| Elastron® G G500.A45.N.PS | Elastron USA, Inc. | SEBS | Elastron® G |
| Koylene ADL-CP AMU120N | Reliance Industries Limited | PP Impact Copolymer | Koylene ADL-CP |
| Huafon JF-P-5175 / JF-I-5118 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| Softell TKG 300N C12616 | LyondellBasell Industries | PP Copolymer | Softell |