Spartech Polycom 6070G100

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	Spartech Polycom
Trademark:	Spartech
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	U2nz6i_Spartech-Polycom-6070G100.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Spartech Polycom 6070G100 is a polypropylene homopolymer (PP Homopoly) product, which contains 20% talc filler. It is available in North America.

Features include:

odorless/tasteless channel

Good processability

Homopolymer

Good stiffness

General Information
Filler / Reinforcement	Talc filler, 20% filler by weight
Features	Rigid, good Homopolymer Workability, good The smell is low to none The smell is low to none
Appearance	White
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.04	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	8.0	g/10 min	ASTM D1238
Molding Shrinkage - Flow (3.18 mm)	1.5	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield, 23°C)	31.7	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield, 23°C	4.0	%	ASTM D638
Fracture, 23°C	30	%	ASTM D638
Flexural Modulus - Tangent (23°C)	2410	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	27	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, not annealed	118	°C	ASTM D648
1.8 MPa, not annealed	68.3	°C	ASTM D648

Resin Grade	Manufacturer	Category	Trademark
Sumikon® EME-6300HN	Sumitomo Bakelite Co., Ltd.	Epoxy	Sumikon®
3M™ Dyneon™ PTFE TF 2025Z	3M Advanced Materials Division	PTFE	3M™ Dyneon™ PTFE
Crastin® S650FR NC010	DuPont Performance Polymers	PBT	Crastin®
Electrafil® PA6 CF20 BK	Techmer Engineered Solutions	Nylon 6	Electrafil®
Polaris™ MR 80499-18	Ashland Performance Materials	Polyester, TS	Polaris™