Sunny® PET EN230
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Guangdong Shunde Shunyan New Material Co., Ltd. |
| Trademark: | Sunny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LNS8LW_Sunny-PET-EN230.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EP Flame retardant reinforced polybutylene terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.65 | g/cm³ | ASTM D792 |
| 23°C | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.30 to 0.60 | % | ASTM D955 |
| 23°C | 0.30 to 0.60 | % | ISO 294-4 |
| Water Absorption | |||
| Equilibrium, 23°C | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- 2 | 100 | MPa | ASTM D638 |
| -- | 100 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.9 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span | 5820 | MPa | ASTM D790 |
| 50.0 mm Span | 6000 | MPa | ISO 178 |
| Flexural Strength | |||
| 50.0 mm Span | 145 | MPa | ASTM D790 |
| -- 4 | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 220 | °C | ASTM D648, ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 250 | °C | |
| Front Temperature | 245 | °C | |
| Processing (Melt) Temp | 255 | °C | |
| Mold Temperature | 90.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 50 mm span |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J106G | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| Sindustris PP EI5003 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Spartech Polycom SS1070U | Spartech Polycom | ASA | Spartech |
| Zhongfa PP pp2 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Geon™ Vinyl Rigid Extrusion 87180 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |