COSMOPLENE® AX191
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOPLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TkplZ3_COSMOPLENEAX191.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COSMOPLENE AX191 is a high impact PP copolymer manufactured by the latest gas phase process licensed from Sumitomo Chemical Co. Japan. It exhibits good impact property at high melt flow rate. COSMOPLENE AX191 also shows excellent flowability and good surface appearance of parts after molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 50 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal method | ||
| Flow : 2.00mm | 1.6 | % | Internal method |
| Transverse flow : 2.00mm | 1.6 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 65 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 20.0 | MPa | ASTM D638 |
| Fracture | 16.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 930 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 65 | J/m | ASTM D256 |
| 23°C | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 117 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 190 - 230 | °C | |
| Front Temperature | 190 - 230 | °C | |
| Mold Temperature | 30 | °C | |
| Injection Pressure | 6.86 | MPa | |
| Clamp Tonnage | 0.98 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unilex™ UP 1112C | United Polychem | PP Random Copolymer | Unilex™ |
| Zytel® 103HSL NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Adell PS IV-11-N | Adell Plastics, Inc. | PS (HIPS) | Adell PS |
| Sylvin 7833-85 White 1574 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ FE1520PW resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |