LNP™ LUBRICOMP™ Lexan_LF1520A compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TkVD1Y_LNPLUBRICOMPLexanLF1520Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% glass reinforced/15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.15 - 0.25 | % | Internal method |
| Transverse flow : 3.20mm | 0.20 - 0.45 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 93.1 | MPa | ASTM D638 |
| Fracture | 93.1 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 5.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 6210 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 148 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 17.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 133 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 128 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 5.2E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 5 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYLON® 235N | Tyne Plastics LLC. | Nylon 6 | TYLON® |
| Westlake MDPE EB171 | Westlake Chemical Corporation | MDPE | Westlake MDPE |
| Ultra Low Outgassing™ SCV-2596 | NuSil Technology | Silicone | Ultra Low Outgassing™ |
| Hifax TYC 852P E S82786 | LyondellBasell Industries | PP Copolymer | Hifax |
| REPOL® SS80N | Reliance Industries Limited | PP Homopolymer | REPOL® |