K-Prene XL-A60
| Category: | PP+EPDM , Polypropylene + EPDM Rubber |
| Manufacturer: | Technovinyl Polymers India Ltd. |
| Trademark: | K-Prene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TkIgtP_K-Prene-XL-A60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| K-Prene XL-A60 is a polypropylene EPDM rubber (PP EPDM) material,. This product is available in Africa and the Middle East,. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 60 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set 1(23°C) | 13 | % | ASTM D412 |
| Tensile Stress | ASTM D412 | ||
| 100% strain | 1.50 | MPa | ASTM D412 |
| 300% strain | 3.00 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 5.50 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 550 | % | ASTM D412 |
| Tear Strength | 20.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 70°C, 22 hr | 40 | % | ASTM D395 |
| 100°C, 22 hr | 50 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ozone Resistance - 70 hrs | Pass |
| Note Message | |
|---|---|
| 1 . | 10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC7-7006U | Spartech Polycom | PC | Spartech |
| TRIBIT® 1500G10K | Samyang Corporation | PBT | TRIBIT® |
| Geon™ Vinyl Dry Blend E1354 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |
| Electroblend® PP-1800 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP Homopolymer | Electroblend® |
| ESTABLEND 8500 V0 HF | Cossa Polimeri S.r.l. | ASA+PC | ESTABLEND |