NORYL™ V0150B resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TghxMi_NORYLV0150Bresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL V0150B is an unfilled, injection moldable modified polyphenylene ether resin.. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 1.5 mm and a UL94 5Va rating at 2.0 mm. NORYL V0150B is also halogen free according to VDE/DIN 472 part 815 and may be an excellent material candidate where flame resistance and high temperature resistance is required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 3.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | Internal method | ||
| -- 1 | 0.50 - 0.70 | % | Internal method |
| 3.20 mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.18 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 113 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2500 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 70.0 | MPa | ASTM D638 |
| Yield | 70.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 60.0 | MPa | ASTM D638 |
| Fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 5.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Fracture 6 | 7.0 | % | ASTM D638 |
| Fracture | 10 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 7 | 2550 | MPa | ASTM D790 |
| -- 8 | 2400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 110 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 105 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 35.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10 | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 14 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 180 | J/m | ASTM D256 |
| 23°C | 330 | J/m | ASTM D256 |
| -30°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 13 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 50.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 100 mm span 13 | 140 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 135 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 14 | 130 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/B120 12 15 |
| -- | 160 | °C | ISO 306/A50 |
| -- | 145 | °C | ISO 306/B50 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | IEC 60695-10-2 | |
| 140°C 16 | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.27 | W/m/K | ISO 8302 |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 115 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 33 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 26 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.80 | IEC 60250 | |
| 60 Hz | 2.80 | IEC 60250 | |
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 9.0E-4 | IEC 60250 | |
| 60 Hz | 9.0E-4 | IEC 60250 | |
| 1 MHz | 3.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | IEC 60695-2-13 |
| 2.00 mm | 775 | °C | IEC 60695-2-13 |
| 3.00 mm | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Hopper Temperature | 80.0 - 100 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 280 - 300 | °C | |
| Processing (Melt) Temp | 300 - 320 | °C | |
| Mold Temperature | 100 - 130 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 120*10*4 mm |
| 14 . | 120*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| 16 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hostacom PPU X9067HS | LyondellBasell Industries | PP Copolymer | Hostacom |
| LAPEROS® E477i | Polyplastics Co., Ltd. | LCP | LAPEROS® |
| LNP™ THERMOCOMP™ RF007SXP compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| LNP™ LUBRICOMP™ RA004 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| LEXAN™ HFD1810 resin | SABIC Innovative Plastics | PC | LEXAN™ |