Stanyl® TW271B6
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 01Wy0s_Stanyl-TW271B6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stanyl® TW271B6 is a Polyamide 46 (Nylon 46) material filled with 30% carbon fiber. It is available in Asia Pacific, Europe, or North America. Primary attribute of Stanyl® TW271B6: Heat Stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 24000 | 14500 | MPa | |
| 120°C | 13500 | -- | MPa | |
| 160°C | 12000 | -- | MPa | |
| 180°C | 11500 | -- | MPa | |
| 200°C | 11000 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break | 260 | 170 | MPa | |
| Break, 120°C | 140 | -- | MPa | |
| Break, 160°C | 115 | -- | MPa | |
| Break, 180°C | 105 | -- | MPa | |
| Break, 200°C | 95.0 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break | 1.7 | 3.5 | % | |
| Break, 120°C | 3.1 | -- | % | |
| Break, 160°C | 3.1 | -- | % | |
| Break, 180°C | 3.1 | -- | % | |
| Break, 200°C | 3.1 | -- | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | 7.0 | kJ/m² | |
| 23°C | 7.0 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 55 | kJ/m² | |
| 23°C | 50 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 3.5E-5 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 305 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene GC35P200-01UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Cheng Yu PP225 | Cheng Yu Plastic Company Limited | PP, Unspecified | Cheng Yu |
| Kumho KBR 710H | Korea Kumho Petrochemical Co., Ltd. | PBR, Low Cis | Kumho KBR |
| Karina BLACK PVC COMPOUND 970-DA-48/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hifax TYC 258P C1V301 | LyondellBasell Industries | PP Copolymer | Hifax |