Tecomid® NA40 GR25 NL HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecomid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TUh4KK_Tecomid-NA40-GR25-NL-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA6.6, 25% glass fiber reinforced, heat stabilized, natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 1.1 | % | Internal method |
| Flow direction | 0.30 | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | % | ISO 62 |
| Moisture Content | % | ISO 15512 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | Low |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 60 | kJ/m² | ISO 180/1U |
| 23°C | 65 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 255 | °C | ISO 306/B |
| Melting Temperature 1 | 262 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 70.0 - 110 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 100 | MPa |
| Injection instructions |
|---|
| Pre-drying is not necessary for materials in moisture proof closed bags. |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4560 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| PRIMATOP HDPE 200952 | Amco Polymers | HDPE | PRIMATOP |
| Ferro PP LPP40BD09WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| JSR EPR EP57P | JSR Corporation | EPDM | JSR EPR |
| Karina GREEN PVC COMPOUND 550-40/61-IS-SD (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |