Torelina® A674M2
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Toray Resin Company |
| Trademark: | Torelina® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TUgkkt_Torelina-A674M2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Torelina® A674M2 is a Polyphenylene Sulfide (PPS) product filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.75 | % | |
| Flow : 3.00 mm 2 | 0.15 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.1 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 12000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 225 | MPa | ISO 178 |
| Shear Strength (23°C) | 65.0 | MPa | JIS K7214 |
| Coefficient of Friction 3 | 0.25 | ||
| Taber Abrasion Resistance (1000 Cycles) | 50.0 | mg | ISO 9352 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 57 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Melting Temperature | 278 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.8E-5 | cm/cm/°C | |
| Transverse | 2.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 24 | kV/mm | IEC 60243-1 |
| Dielectric Constant 4(23°C, 1 MHz) | 3.90 | IEC 60250 | |
| Dissipation Factor 5(23°C, 1 MHz) | 3.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 6(320°C, 1.00 mm) | 125 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | vs. Metal |
| 4 . | 60% RH |
| 5 . | 60% RH |
| 6 . | 98 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BK10NT6529 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Ultraform® W 2320 003 BK120 Q600 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| MAJORIS AFR992 - 8229 | AD majoris | PP Copolymer | MAJORIS |
| 3M™ Dyneon™ Fluoroelastomer FE 5520 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Sylvin 2900-80 Clear Black 291 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |