GECET™ 5501
| Category: | PS (EPS) , Expanded Polystyrene |
| Manufacturer: | Fagerdala USA Inc. |
| Trademark: | GECET™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sy6LfC_GECET-5501.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Grade 5501 is a regular grade, black-pigmented expandable polystyrene resin. This resin is specifically formulated for high-density, impact absorption applications such as bicycle helmet liners. Grade 5501 resin is available in an unexpanded particle size range of 0.6 - 1.2 mm, and the typical density range for molded application is 2.5 to 10 pcf. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | ASTM C203 | ||
| -- 1 | 29.6 | MPa | |
| -- 2 | 20.0 | MPa | |
| Flexural Strength | ASTM C203 | ||
| -- 3 | 1.03 | MPa | |
| -- 4 | 0.655 | MPa | |
| Compressive Strength | ASTM D1621 | ||
| 10% Strain 5 | 0.455 | MPa | |
| 10% Strain 6 | 0.283 | MPa | |
| 15% Strain 7 | 0.483 | MPa | |
| 15% Strain 8 | 0.303 | MPa | |
| 20% Strain 9 | 0.524 | MPa | |
| 20% Strain 10 | 0.331 | MPa |
| Note Message | |
|---|---|
| 1 . | 3.5 lbs/ft³ |
| 2 . | 2.5 lbs/ft³ |
| 3 . | 3.5 lbs/ft³ |
| 4 . | 2.5 lbs/ft³ |
| 5 . | 3.5 lbs/ft³ |
| 6 . | 2.5 lbs/ft³ |
| 7 . | 3.5 lbs/ft³ |
| 8 . | 2.5 lbs/ft³ |
| 9 . | 3.5 lbs/ft³ |
| 10 . | 2.5 lbs/ft³ |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BJB Epoxy TC-1606 A/B | BJB Enterprises, Inc. | Epoxy | BJB Epoxy |
| Flontech® FT-BRR55-M5-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| K-vinyl 105 Deg C Rating Insulation (85-Dry) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| IROCOAT® CA-330 | Huntsman Corporation | TPU, Unspecified | IROCOAT® |
| Karina MBPEB WHITE-E 1000/6000-IE | Karina Ind. e Com. de Pl谩sticos Ltda | PVC, Unspecified | Karina |