LNP™ LUBRICOMP™ UCL36S compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sx3Kq2_LNP-LUBRICOMP-UCL36S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP UCL36S is a compound based on Polyphthalamide resin containing 15% PTFE, 30% Carbon Fiber. Added features of this material include: Wear Resistant, Heat Stabilized, Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound UCL-4036 HS Product reorder name: UCL36S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 20100 | MPa | ASTM D638 |
| Tensile Strength | |||
| Break | 216 | MPa | ASTM D638 |
| Break | 214 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.6 | % | ASTM D638 |
| Break | 1.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 18800 | MPa | ASTM D790 |
| -- | 22700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 324 | MPa | ASTM D790 |
| -- | 334 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.36 | ||
| vs. Itself - Static | 0.27 | ||
| Wear Factor - Washer | 16.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 8.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 940 | J/m | ASTM D4812 |
| 23°C 3 | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 279 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 149 to 171 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 802 SI 2 | RTP Company | Acetal (POM) Copolymer | RTP |
| Tufel® II 94706 | Momentive Performance Materials Inc. | Silicone | Tufel® II |
| Niche PPCM6BK | Niche Polymer, LLC | PP Copolymer | Niche |
| ExxonMobil™ LDPE LD 258 | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Sylvin 8225-80 White 1468 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |