INELEC PPHF
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INELEC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hyZ7MO_INELEC-PPHF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ELECTRICALLY CONDUCTIVE, HIGH FLOW POLYPROPYLENE |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.3 to 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 24.8 | MPa | ASTM D638 |
| Flexural Modulus | 1240 | MPa | ASTM D790 |
| Flexural Strength | 31.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 480 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+7 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 193 | °C | |
| Mold Temperature | 37.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.013 to 0.025 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TW250F6 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| CLARIX® 111702-01 Clear | A. Schulman Inc. | Ionomer | CLARIX® |
| Dugdale PVC Rigid Extrusion Black Compound | Dugdale Plc | PVC, Rigid | Dugdale PVC |
| Hylon® N1000EL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| INSTRUC PPSBGF40IM | Infinity LTL Engineered Compounds | PPS | INSTRUC |