RTP 199 X 123298
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Srn3XT_RTP199X123298.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Impact - Permanently Static Dissipative - ESD Protection - UV Stabilized |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 - 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 - 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 965 | MPa | ASTM D638 |
| Tensile Strength | 17.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 827 | MPa | ASTM D790 |
| Flexural Strength | 24.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 800 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+7 - 9.9E+8 | ohms | ESD STM11.11 |
| -- | 1.0E+8 - 9.9E+9 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+7 - 9.9E+8 | ohms·cm | ASTM D257 |
| Static Decay 1 | sec | FTMS 101C 4046.1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 171 - 204 | °C | |
| Mold Temperature | 32 - 66 | °C | |
| Injection Pressure | 48.3 - 75.8 | MPa |
| Injection instructions |
|---|
| Do not exceed 520 °F (270 °C) melt temperature.Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | MIL-PRF-81705D, 5kV to 50 V, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIREX® Compound HF3000HG10 | Samyang Corporation | PC | TRIREX® Compound |
| Celcon® CF802 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| GPPC ABS D-1000 | GPPC Chemical Co., Ltd. | ABS | GPPC ABS |
| LUVOCOM® 1105-8234 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Tunhe PBT TH6100F | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBT | Tunhe PBT |