PLEXIGLAS® Satinice df22 7N, based on PLEXIGLAS® 7N, is characterized by diffuse scattering of light. Typical properties of PLEXIGLAS® molding compound are
Special properties of PLEXIGLAS® Satinice df22 7N are
Application: Used for injection molding items for lighting engineering applications Examples: applications that call for light diffusion combined with optimum transmission |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 4.30 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 65.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.8 | kJ/m² | ISO 179/1 |
| Charpy Unnotched Impact Strength (23°C) | 17 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 101 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 97.0 | °C | ISO 75-2/A |
| Glass Transition Temperature | 108 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 105 | °C | ISO 306/B50 |
| CLTE - Flow (0 to 50°C) | 6.3E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 700 | °C | IEC 60695-2-13 |
| Fire Rating | B2 | DIN 4102 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Half-Value Angle | 12.5 | ° | DIN 5036 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 1 | 86.0 | % | ISO 13468-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 95.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Melt Temperature | 220 to 260 | °C | |
| Die Temperature | 220 to 260 | °C |
| Note Message | |
|---|---|
| 1 . | D65 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8627-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VESTAMID® L L1930 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| TIPOLEN® FD 243-51 | MOL Petrochemicals Co. Ltd. | LDPE | TIPOLEN® |
| Generic PF - Glass Fiber | Generic | PF | Generic |
| Hiflex CA 7600 A | LyondellBasell Industries | TPO (POE) | Hiflex |