Diakon® ST15G7L
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Inc. |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SdSCpC_Diakon-ST15G7L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diakon® ST15G7L is a Polymethyl Methacrylate Acrylic material. It is available in Europe for injection molding. Important attributes of Diakon® ST15G7L are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 6.6 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.31 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 84 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 74.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 7.0 | % | ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Flexural Stress | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 22 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 2.1 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 107 | °C | ISO 306/A |
| -- | 100 | °C | ISO 306/B |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ISO 489 | |
| Transmittance | 91.5 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 250 | °C | |
| Middle Temperature | 200 to 270 | °C | |
| Front Temperature | 210 to 280 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R550H NT453 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| XAREC™ C122 | Idemitsu Kosan Co., Ltd. | SPS | XAREC™ |
| Fiberfil® J-60/30/E3 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| MAJORIS CFR269 - 1333 | AD majoris | PP, Unspecified | MAJORIS |
| Delene 2050 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |