Plaslube® PC CF10 TL15 FR BK
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sb7GmX_Plaslube-PC-CF10-TL15-FR-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube®PC CF10 TL15 FR BK is a polycarbonate (PC) product that contains 10% carbon fiber reinforcement. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.35 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 108 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.26 | ASTM D1894 | |
| With steel-static | 0.19 | ASTM D1894 | |
| Wear Factor | 75 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 147 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 143 | °C | ASTM D648 |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+8 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+8 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 302 - 316 | °C | |
| Middle Temperature | 316 - 332 | °C | |
| Front Temperature | 310 - 327 | °C | |
| Nozzle Temperature | 310 - 327 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 71.1 - 87.8 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 799 X 50492 L | RTP Company | HDPE | RTP |
| Vital-Line SHE6545 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Adell PP EA-16 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| Aplax P2213GN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| Osterlene® PPH-100-.3 | Osterman & Company | PP Homopolymer | Osterlene® |