Ultramid庐 B3UM4
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SXagco_Ultramid-B3UM4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced, halogen- and phosphorus free flame retardant injection moulding grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 90.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 to 2.4 | -- | % | ISO 62 |
| Mold Shrinkage - Test box (1.50 mm) | 0.60 | -- | % |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Fire Performance - UL94+HAI+HWI 1 | > 3.00 | -- | mm | UL 746C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Hot Wire Test (3.0 µm) | 1.00 | -- | ASTM D3874 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5300 | 1800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 70.0 | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 40 | 200 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 110 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (> 0.750 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (1.50 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 32 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | For Electrical Insulation/Barrier with close proximity (< 0,8 mm) to uninsulated live parts according to UL 746C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 6600/40 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| Tectron E1177 | TECTRON Systems Pte Ltd | TPV | Tectron |
| TOTAL Polypropylene PPC 9760 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Hangzhou Plastic PVC/PVDC Laminated Film | Hangzhou Plastic Industry Co., Ltd. | Film, PVC/PVDC | Hangzhou Plastic |
| Petlon R-Prime F3-T40-00-BK | Petlon Polymers Ltd | PP, Unspecified | Petlon R-Prime |