Boda BDF2602AP
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SIHqgU_Boda-BDF2602AP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDF2602AP is a medium viscosity curative incorporated fluoroelastomer copolymer. This is a general purpose grade, well suited for application where excellent process property is required. BDF2602AP can be compounded to meet the major fluoroelastomer specifications. BDF2602AP can be used for compression molding of O-rings, gaskets or oil seals or extrusion molding of articles. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 38 | MU | |
| Fluorine Content | 66 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 2.10 | N·m | |
| ML 2(177°C) | 0.260 | N·m | |
| t'90 3(177°C) | 2.0 | min | |
| ts2 4(177°C) | 1.2 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 76 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 13.8 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 220 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 21 | % | ASTM D395B |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBN7584 | Teknor Apex Asia Pacific PTE. LTD. | PP Homopolymer | Sinpolene |
| Surlyn® 1857 | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| VINIKA® CF80EA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Nanjing Hongrui PA66 A500 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Karina GRAY PVC COMPOUND 550-18/363-A | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |